Browsing by Author "Bajpai, Madhu"

Now showing 1 - 2 of 2

Synthesis and characterization of acrylated epoxidized soybean oil for UV cured coatings
(Publishing House of Lviv Polytechnic National University, 2011) Habib, Firdous; Bajpai, Madhu
This paper investigates the curing of biodegradable polymer films which were synthesized from soybean oil through the ultraviolet radiation and their stability against thermal degradation. In this study the epoxidation of soybean oil has been carried out via peracetic method. Further, an epoxy acrylate resin was synthesized from the epoxidized soybean oil (ESO) by using acrylic acid monomer. Triethylamine (TEA) and hydroquinone were used as a catalyst and inhibitor respectively. The acrylation of epoxidized soybean oil (AESO) is done by introducing acrylic acid, which is an unsaturated monomer into oxirane groups of the epoxidized oil (ESO). This reaction was confirmed by analytical data in terms of oxirane oxygen content, acid value, viscosity and spectral analysis. Different UV curable formulations have been investigated using synthesized acrylated resin and trifunctional acrylate monomer used as crosslinkable active diluents with photoinitiator. Monomer used was trimethylolpropane trimethacrylate (TMPTMA) while photoinitiator used was benzophenone along with an activator dimethyl ethanol amine (DEA). The mixtures were cured to make thin polymeric films under UV radiation with optimum irradiation dosing time of 20 min to produce the excellent cured coating which exhibits good thermal stability of about 473 K. В роботі досліджено затвердіння біодеградабельних полімерних плівок, синтезованих з соєвої олії за допомогою ультрафіолетового випромінювання, і їх стійкість до термічного розкладання. Епоксидування соєвої олії проводилось за допомогою надоцтового методу. Синтезовано епоксидну акрилатну смолу з епоксидованої соєвої олії з використанням акрилових мономерів кислоти. Як каталізатор та інгібітор відповідно використано триетиламін і гідрохінон. Акрилування епоксидованої соєвої олії проводилось внаслідок введення акрилової кислоти, яка є ненасиченим мономером, в оксиранові групи олії. Перебіг реакції підтверджено аналітичними даними стосовно вмісту оксиранового кисню, кислотним числом, в'язкістю і спектральними методами аналізу. Досліджено різні УФ-затверджені композиції, використовуючи синтезовані акрилатні смоли і трифункціональні акрилатні мономери як активні активні розчинники, зшиті з фотоініціатором. Як мономер використовували триметилолпропан триметилакрилату, а як фотоініціатор - бензофенон. Активатором слугував диметилетаноламін. Суміші були затверджені під ультрафіолетовим випромінюванням з оптимальним дозуванням опромінення 20 хв. для одержання тонких полімерних плівок, які можуть бути викорситані для виробництва термостійких (вище 473 К) покриттів.
UV curable heat resistant epoxy acrylate coatings
(Publishing House of Lviv Polytechnic National University, 2010) Firdous, Habib; Bajpai, Madhu
Polymeric materials are exposed to high temperatures that results in lowering of the film integrity. A blend of an epoxy resin with the silicone acrylate resin was developed to provide high heat resistance UV cured coatings. Earlier siliconized epoxy coatings had been developed by conventional curing. But due to environmental awareness, high productivity rate, low process costs and energy saving UV curable coatings are enjoying considerable growth. Thermally stable UV cured coatings used in the present study were developed from silicone acrylate and epoxy acrylate resin with different diluents and photoinitiator. Such coatings provide higher thermal stability (693 K) along with physical and chemical resistance. In addition, such coatings can also be obtained by using functional amino silanes. The resin developed provides a simple and practical solution to improve heat resistance along with physical and chemical resistance of the UV cured coatings. The purpose of this research paper is to develop UV curable heat resistant coatings by the combination of inorganic and organic polymer, taking epoxy acrylate as a base resin. В роботі вивчено отримання термостабільних УФ-затверджених покриттів, виходячи з силікон-акрилатів та епоси-акрилатних смол, в присутності різних за природою розчинників іфотоініціаторів. Встановлено, що такі покриття характеризуються високою термостабільністю (693 К) та проявляють фізичну і хімічну стійкість. Запропонований метод дає можливість отримувати термостійкі покриття, виходячи як із органічного, так і неорганічного полімеру, в тому числі функцій них аміносиланів, беручи за основу епоксидний акрилат.