Anodic decomposition of complexing agents in electrolytes based on Cr(III) salts at composite ТіОх/РtОу electrodes
(Publishing House of Lviv Polytechnic National University, 2012) Kasian, Olga; Luk’yanenko, Tatiana; Velichenko, Alexander
The kinetics of complexing agents anodic decomposition in electrolytes based on Cr(III) salts was investigated. In Cr(III) electrolytes urea was shown to be fixed in complexes with Cr3+-ions. It was found that the main way of free carbamide degradation was hydrolysis characterized by a high rate (k = 4.5·10-3 min-1). Decrease in formic acid concentration during electrolysis at composite ТіОх/РtОу-anodes was insignificant. Досліджено кінетику анодного розкладу комп- лексоутворювачів в електролітах на основі солей Cr(III). Показано, що в електролітах хромування на основі солей Cr(III) карбамід зв’язаний у комплекси з Cr 3+-йонами. Встановлено, що основним маршрутом розкладу карбаміду є кислотний гідроліз, який перебігає зі значною швидкістю (k = 4,5·10 -3 хв -1 ). Досліджено зменшення концентрації мурашиної кислоти під час електролізу на композиційних ТіОх /РtОу-анодах.
Influence of Bi3+ ions on kinetics of lead dioxide electrodeposition from methanesulfonate electrolytes
(Publishing House of Lviv Polytechnic National University, 2013) Shmychkova, Olesia; Magamedova, Amina; Girenko, Dmitriy; Luk’yanenko, Tatiana; Velichenko, Alexander
Influence of bismuth ions on kinetics of lead dioxide electrodeposition from methanesulfonate electrolytes on Pt-electrode was studied. Experimental results are interpreted to be consistent with the mechanism proposed previously for lead dioxide electrodeposition in literature. The presence of bismuth ions in the electrodeposition solution causes decreasing rate constants of lead dioxide formation due to additive adsorption. Вивчено кінетику електроосадження діокиду свинцю з метансульфонатних електролітів на Pt у присутності та без йонів бісмуту. Електроосадження перебігає за механізмом, запропонованим в літературі для діоксиду свинцю. У разі введення до електроліту осадження йонів бісмуту константа швидкості гетерогенної реакції утворення діоксиду свинцю знижується через адсорбцію модифікуючої домішки.
PbO2 based composite materials deposited from suspension electrolytes: electrosynthesis, physico-chemical and electrochemical properties
(Publishing House of Lviv Polytechnic National University, 2012) Velichenko, Alexander; Knysh, Valentina; Luk’yanenko, Tatiana; Dmitrikova, Larisa; Velichenko, Yulia; Devilliers, Didier
Composite materials based on PbO2 containing TiO2 or ZrO2 were prepared from electrolytes containing a suspension of TiO2 or ZrO2. The contents of foreign oxides in the composite depend on the electrolyte composition and conditions of deposition. When a dispersed phase is incorporated into the composite coating, the dimensions of lead dioxide crystals decrease to submicro- and nano-size. Physico-chemical properties and electrocatalytic activity of composite materials are mainly determined by their chemical composition. The electrocatalytic properties of a composite PbO2-TiO2 anode vs the oxygen evolution reaction (OER) and the electrochemical degradation of methyl tert-butyl ether (MTBE) were investigated. Композиційні матеріали на основі PbO2, що мають в своєму складі TiO2 або ZrO2, були одержані з суспензійних електролітів з часточками дисперсної фази TiO2 чи ZrO2. Концентрація сторонніх оксидів в композиті залежить від складу електроліту та умов осадження. В процесі залучення часточок дисперсної фази до композиту кристали плюмбум(IV) оксиду зменшуються до субмікроних та нано-розмірів. Фізико-хімічні властивості та електрокаталітична активність композиційних матеріалів у більшості випадків обумовлюється їх хімічним складом. Досліджено електрокатілітичні властивості композиційних анодів PbO2-TiO2 в реакціях виділення кисню та електрохімічного руйнування метил трет-бутилового етеру (МТБЕ).
The Electrodeposition Kinetics of Modified Lead Dioxide
(Видавництво Львівської політехніки, 2013) Shmychkova, Olesia; Luk’yanenko, Tatiana; Velichenko, Alexander
The influence of complex ions on kinetics of lead dioxide electrodeposition from methanesulfonate electrolytes was studied. Experimental results are consistent with a mechanism previously proposed in literature for lead dioxide electrodeposition. The presence of ions involved in the electrodeposition solution causes a decrease of rate constants of lead dioxide formation due to co-adsorption phenomena. Oxygen evolution was investigated to test electrocatalytic activity. It is shown, that oxygen overpotential on modified electrodes is significantly higher than on non-modified PbO2-electrode.