Zhyltsova, SvitlanaMykhalchuk, VolodymyrPlatonova, OlgaBiloshenko, Victor2011-12-262011-12-262011Epoxy-silica nanocomposites based on ethoxysilanes and diglycidyl ether of dicyclohexylpropane / Svitlana Zhyltsova, Volodymyr Mykhalchuk, Olga Platonova, Victor Biloshenko // Chemistry & Chemical Technology. – 2011. – Volume 5, number 1. – P. 49–54. – Bibliography: 18 titles.https://ena.lpnu.ua/handle/ntb/11213Sol-gel method was used to obtain epoxy-silica nanocomposites cured with dicarboxylic acid anhydride. Incorporation of filler into the system leads to plastisization of organic matrix: glass transition temperature decreases and sol-faction yield increases with filler content. At w(SiO2) = 0.5–3 mas % effect of low additions is observed: molecular weight of chain between junctions decreases and thermostability of hybrid materials rises. Золь-гель методом одержано епоксидно-силоксанові нанокомпозити ангідридного тверднення. Встанов-лено, що при введенні в систему наповнювача відбуваєтьсяпластифікація органічної матриці: знижується температурасклування, збільшується вихід золь-фракції. При концентраціїSiO2 0.5–3 мас % проявляється ефект малих добавок: спосте-рігається зниження молекулярної маси міжвузлових ланцюгів іпідвищення термостабільності гібридних матеріалів.enepoxy-silica nanocompositesanhydride curingsol-gel methodепоксидно-силоксанові нанокомпозитиангідридне твердненнязоль-гель методArticle