Bratychak, MichaelBashta, BogdanaBruzdziak, PiotrAstakhova, OlenaShyshchak, Olena2013-04-172013-04-172013Cross-linking of epoxy-oligoesteric mixtures in the presence of carboxy-containing derivative of ED-24 epoxy resin / Michael Bratychak, Bogdana Bashta, Piotr Bruzdziak, Olena Astakhova, Olena Shyshchak // Chemistry & Chemical Technology. – 2013. – Volume 7, number 1. – P. 41–46. – Bibliography: 7 titles.https://ena.lpnu.ua/handle/ntb/18291Cross-linking of epoxy-oligomeric mixtures has been studied at room temperature and at heating to 383,403 and 423 K for 15, 30, 45, 60 and 75 min in the presence of polyethylenepolyamine. The mixtures consist of industrial ED-20 epoxy resin,oligoesteracrylate TGM-3 and carboxy-containing derivative of ED-24. The effect of mixture composition, temperature and process time on the gel-fraction content and hardness of polymeric films has been examined. Using IR-spectroscopy the chemism of network formation has been determined. Вивчено структурування за кімнатної температури і при нагріванні до 383, 403 або 423 К впродовж 15, 30, 45, 60 і 75 хв. епокси-олігоестерних сумішей, що складаються з промислової епоксидної смоли ЕД-20,олігоестеракрилату ТГМ-3 і карбоксилвмісної похідної епоксидної смоли ЕД-24 (КПЕС) в присутності поліетиленполіаміну. Встановлено вплив складу суміші, температури і тривалості структурування на вміст гель-фракції в зразках та твердість полімерних плівок. З використанням ІЧ спектроскопії встановлено хімізм утворення просторовозшитих структур.enepoxy resinoligoesteracrylatecarboxy groupIR-spectroscopyacid numbercross-linkingcross-linkingfilm hardnessепоксидна смолаолігоестеракрилаткарбоксильна групакислотне числоструктуруванняІЧ спектроскопіягель-фракціятвердість плівокCross-linking of epoxy-oligoesteric mixtures in the presence of carboxy-containing derivative of ED-24 epoxy resinСтруктурування епокси-олігоестерних сумішей в присутності карбоксилвмісної епоксидної похідної смоли ЕД-24Article