Dzyazko, YuliyaPonomarova, LudmilaVolfkovich, YuriiTsirina, ValentinaSosenkin, ValentinNikolska, NadiyaBelyakov, Volodimir2016-12-202016-12-202016Influence of zirconium hydrophosphate nanoparticles on porous structure and sorption capacity of the composites based on ion exchange resin / Yuliya Dzyazko, Ludmila Ponomarova, Yurii Volfkovich, Valentina Tsirina, Valentin Sosenkin, Nadiya Nikolska, Volodimir Belyakov // Chemistry & Chemical Technology. – 2016. – Volume 10, number 3. – P. 329–335. – Bibliography: 15 titles.https://ena.lpnu.ua/handle/ntb/34753Evolution of swelling of gel-like strongly acidic resin and organic-inorganic composites based on this ionexchanger was investigated. Non-aggregated nanoparticles of zirconium hydrophosphate were found to provide size invariability of the polymer pores, which contain functional groups (up to 20 nm), the nanoparticle aggregates squeeze these pores (down to 3 nm). Owing to this, the nanocomposite shows higher break-through capacity during removal of Ni2+ from water, than the sample modified only with aggregates. Досліджено еволюцію набухання гелевої сильнокислотної смоли та органо-неорганічних композитів на її основі. Знайдено, що неагреговані наночастинки гідрофосфату цирконію, інкорпоровані до полімеру, забезпечують незмінність розміру його пор, які містять функціональні групи (до 20 нм), а агрегати наночастинок здавлюють ці пори (до 3 нм). Зважаючи на це, нанокомпозит демонструє більш високу здатність до проскоку при вилученні йонів Ni2+ з води, ніж зразок, модифікований тільки агрегатами.enorganic-inorganic ion exchangersnanoparticleszirconium hydrophosphatepolymer porositystandard contact porosimetryоргано-неорганічні йонітинаночастинкигідрофосфат цирконіюпористість полімеруеталонна контактна порометріяArticle