Sharanda, MykhailoSontsev, VladyslavBondarenko, EvgeniyaBrei, Volodymyr2015-06-112015-06-112015Two-stage conversion of glycerol into propylene glycol over Cu/Al2O3 catalyst / Mykhailo Sharanda, Vladyslav Sontsev, Evgeniya Bondarenko, Volodymyr Brei // Chemistry & Chemical Technology. – 2015. – Volume 9, number 2. – P. 171–174. – Bibliography: 16 titles.https://ena.lpnu.ua/handle/ntb/28254The conversion of 30 % glycerol mixture in ethanol over Cu/Al2O3 catalyst at 493 K/0.1MPa was studied under Ar-H2 flow with different H2 content. It was shown, that 84 % selectivity towards hydroxyacetone is achieved at using 2.5 % H2 concentration in a carrier gas. Then the product obtained at 493 K has been hydrogenated into a propylene glycol at 448 K in pure H2 flow under 1.2 MPa. 89 % selectivity towards propylene glycol was achieved at moderate consumption of hydrogen H2/C3H6O2 = 4 (mol). Two-stage conversion of glycerol into the propylene glycol at different pressure is proposed. Досліджено перетворення 30% розчину гліцерину в етанолі на Cu/Al2O3 каталізаторі при 493 K/0,1 МПа в потоці Ar-H2 з різним вмістом Н2. Показано, що 84% селективність за гідроксиацетоном досягається при концентрації H2 в газі-носії 2,5%. Проведено гідрування отриманого продукту в пропіленгліколі при температурі 448 К в потоці чистого H2 при 1,2 МПа. При середній витраті водню H2/C3H6O2 = 4 моль досягнуто 89% селективності відносно пропіленгліколю. Показана можливість двостадійного перетворення гліцерину в пропіленгліколь за різних тисків.englycerol dehydrationCu/Al2O3 catalysthydroxyacetonepropylene glycolдегідрований гліцеринкаталізатор Cu/Al2O3гідроксиацетонпропіленглікольArticle