Investigation of phase separation processes for bioactive glasses in Na2О–CаO–ZnO–TiO2–ZrO2–Al2O3–B2O3–P2O5

Savvova, OksanaBabich, Elena2015-06-112015-06-112015Savvova O. Investigation of phase separation processes for bioactive glasses in Na2О–CаO–ZnO–TiO2–ZrO2–Al2O3–B2O3–P2O5–SiO2 system / Oksana Savvova, Elena Babich // Chemistry & Chemical Technology. – 2015. – Volume 9, number 2. – P. 187–192. – Bibliography: 11 titles.https://ena.lpnu.ua/handle/ntb/28251Nanostructural changes on initial stages of calcium silicophosphate glasses nucleation in Na2О–CаO–ZnO–TiO2–ZrO2–Al2O3–B2O3–P2O5–SiO2 system during phase separation have been investigated. It has been established that the presence of drop-shaped nano- and micro-nonuniformities in the structure of calcium silicophosphate glasses substantially affects the glass separation in a precrystallization period, helping intense fine hydroxyapatite crystallization with the crystal size of up to 1 μm after heat treatment. Досліджено наноструктурні зміни на початкових стадіях зародкоутворення в біоактивному кальцій-силікофосфатному склі системи Na2О–CаO–ZnO–TiO2–ZrO2–Al2O3–B2O3–P2O5–SiO2 в процесі фазового розділення. Встановлено, що пристуність краплеподібних нано- і мікронеоднорідностей в структурі кальційсилікофосфатного скла має суттєвий вплив на розшарування скла в докристалізаційному періоді, що сприяє інтенсивній тонко дисперсній кристалізації гідроксиапатиту з розміром кристалів до 1 мкм після термооброблення.ennanostructureliquationcalcium silicophosphate glass-ceramic materialsbone endoprostheticsнаноструктуралікваціякальцій-силікофосфатний скло-керамічний матеріалендопротезування кістокInvestigation of phase separation processes for bioactive glasses in Na2О–CаO–ZnO–TiO2–ZrO2–Al2O3–B2O3–P2O5–SiO2 systemВивчення процесівфазового розділення в біоактивному склі системи Na2О–CаO–ZnO–TiO2–ZrO2–Al2O3–B2O3–P2O5–SiO2Article