    Розробка зносостійких наплавлених шарів для захисту деталей від газоабразивного зношування
    (КІНПАТРІ ЛТД, 2013) Войтович, Андрій; Похмурська, Ганна; Шрайбер, Т.
    The gas abrasive wear resistance of surfaced layer on low carbon steel from cored wires C10Cr5MnSi, 70Cr4Mg2Si2B, 12Cr12Mn2SiVaB, 70Cr20B3Тi have been researched. The maximum wear resistance have surfaced layer from cored wires 70Cr2B3Ti which inherent the austenitic structure with small inclusion of carboborides (Сr)23(ВС)6.
  • Thumbnail Image
    Item
    Розробка зносостійких наплавлених шарів із порошкових дротів для підвищення ресурсу роботи лопаток колеса млинового вентилятора
    (Видавництво Львівської політехніки, 2013) Войтович, Андрій; Головчук, Мирослав
    The aim of the work is to conduct a comparative analysis of durability of the over welded layers with four commercially available boron-containing cored wires (150B6Tі10, 150Cr10B2VМn, 90Cr12SiB, 70Cr20B3Ti). All investigated coatings have been developed in order to increase the operating time and to reduce the maintaince period of the mashine parts that operate under the conditions of the severe abrasive wear. The microstructure and microhardness of the layers have been investigated on the cross-sections. A resistance against abrasion wear has been tested by an operating temperature of 150 °C and the velocity of abrasive particles (200 μm sand) of 36 m/s. It was found that the average hardness of the clad layers due to the formation of the carbides and borides rises to the values of 642 – 1028 HV0.2. The highest values were measured for 150Cr10B2VМn layers and the lowest – for 150B6Tі10 layers. The last can be explained by the formation of the crack network in the hard boron rich matrix. The maximal abrasion wear resistance was observed for the layers with a matrix with austenitic microstructure and carbide inclusions. The best 150B6Tі10 coatings demonstrate an increase in abrasion resistance more than twice if to compare with a substrate 10CrSiNiMn material.