Browsing by Author "Ioni, Yulia"

Now showing 1 - 2 of 2

Nanostructural characteristics of polymer adsorption layers formed under ultrasonic treatment on metal oxides surface in aqueous dispersions
(Publishing House of Lviv Polytechnic National University, 2011) Bulychev, Nikolay; Kisterev, Edward; Ioni, Yulia; Dirnberger, Klaus; Zubov, Vitali; Eisenbach, Claus
The course and the result of the surface modification of titanium dioxide and ferrous oxide pigments in aqueous dispersion by ethylhydroxyethylcellulose (EHEC) without and with mechanical treatment of the dispersion by ultrasonic power was studied by the electrokinetic sonic amplitude (ESA) method. The evaluation of the ESA data showed that the ultrasonic treatment causes a significant thickness increase of the EHEC layer on the pigment which is primarily attributed to the ultrasonically induced activation of the pigment surface. The thickness of the polymer adsorption layer derived from ESA measurements was confirmed by TEM investigations. The ultrasonic treatment leads to significant changes of the adsorption layers properties and is a promising method for the surface modification of pigments with regard to dispersion stability. За допомогою електрокінетичної звукової амплітуди (ЕЗА) досліджено процес модифікації поверхні пігментів діоксиду титану та оксиду заліза у водних дисперсних системах при введенні етилгідроксиетилцелюлози (ЕГЕЦ) у відсутності та в присутності механічного оброблення дисперсних систем ультразвуком. Інтерпретацією даних ЕЗА показано, що ультразвукове оброблення викликає суттєве збільшення товщини шару ЕГЕЦ на поверхні пігментів, що пояснюється ультразвуковою активацією поверхні. Дані про товщину шарів, oтримані методом ЕЗА, підтверджені дослідженнями з використанням просвічуючої електронної мікроскопії. Ультразвукове оброблення призводить до значних змін характеристик адсорбційних шарів і є перспективним методом для модифікування поверхні пігментів та підвищення стабільності дисперсних систем.
Surface modification in aqueous dispersions with thermo-responsive poly(methylvinylether) copolymers in combination with ultrasonic treatment
(Publishing House of Lviv Polytechnic National University, 2011) Bulychev, Nikolay; Kisterev, Edward; Ioni, Yulia; Confortini, Ondine; Du Prez, Filip; Zubov, Vitali; Eisenbach, Claus
The process of surface modification of hydrophobic organic pigments (copper phthalocyanine (CuPc) and carbon black) as well as a hydrophilic inorganic pigment (titanium dioxide) in aqueous dispersions by employing tailor-made thermo-responsive copolymers, and the colloidal stability have been studied. The pigment surface modification is achieved by conventional adsorption and by (thermo)precipitation of amphiphilic methyl vinyl ether (MVE) containing polyvinylether block and PMVE graft copolymers with poly(ethylene oxide) side chains exhibiting a lower critical solution temperature (LCST). The effect of mechanical treatment of the pigment dispersion by ultrasonic power alone or in combination with the LCST property was investigated. The course of the pigment surface coating process was followed by the Electrokinetic Sonic Amplitude (ESA) method. The temperature controlled sorption of PMVE-g-PEO graft copolymers on both inorganic and organic pigment surface was investigated. It was found that ultrasonic treatment together with LCST thermoprecipitation is a promising method for the surface modification of pigments with regard to dispersion stability. Досліджено процес модифікації поверхні гідрофобних органічних пігментів (фталоціаніну міді та сажі) і гідрофільного неорганічного пігменту діоксиду титану у водних дисперсних системах з використанням спеціально синтезованих термочутливих кополімерів та колоїдна стабільність отриманих дисперсних систем. Модифікація поверхні пігментів проводилась звичайною адсорбцією і термоосадженням амфіфільних блочних і прищеплених кополімерів метилвінілового етеру, які містять сегменти оксиду поліетилену та мають нижню критичну температуру розчинності (НКТР). Досліджено вплив ультразвукового оброблення дисперсних систем пігментів у поєднанні з використанням властивостей НКТР. Процес модифікації поверхні пігментів досліджено за допомогою електрокінетичної звукової амплітуди. Досліджено процес температурно-контрольованої сорбції прищеплених кополімерів ПМВЕ-g-ПЕО на поверхні неорганічних і органічних пігментів. Встановлено, що ультразвуковий вплив у поєднанні з термоосадженням є перспективним способом модифікації поверхні пігментів і одержання дисперсних систем високої стабільності.