Growth of thick epitaxial yag:Cr4+ films for passive q-switching of microchip lasers
(Видавництво національного університету „Львівська політехніка”, 2009) Syvorotka, I. I.; Syvorotka, I. M.; Ubizskii, S. B.
Growth peculiarities and magnetic properties of (LuBi)3Fe5O12 films by LPE method
(Видавництво Львівської політехніки, 2012) Syvorotka, I. I.; Syvorotka, I. M.; Ubizskii, S. B.
The series of (LuBi)3Fe5O12 film were grown on (111) oriented GGG substrate with diameters 1, 2 and 3 inch by liquid phase epitaxy using Bi2O3-base flux. Different types of surface morphology on the grown films were observed. The films’ surface was smooth and mirror while the film thickness was less than 13 μm and becomes rough for thickness above this value. The grown films were characterized by measuring magnetization loops and magneto-optic Faraday rotation under magnetization reversal as well as ferromagnetic resonance (FMR). All films with mirror surface demonstrate the in-plane magnetization, high Faraday rotation and FMR linewidth about 0.8 Oe at 9.1 GHz and room temperature.
Hизькотемпературні DC-вимірювання супермагнітних наноматеріалів за допомогою устаткування PPMS
(Видавництво Львівської політехніки, 2012) Demchenko, P. P.; Ubizskii, S. B.; Ślawska-Waniewska, A.
Luminescent and Structural Studies of Y3Al5O12 Nanopowders Doped with Different Concentrations of Yb3+ Ions
(2017-05-29) Syvorotka, I. I.; Luchechko, A. P.; Sugak, D. Yu.; Vasylechko, L. O.; Zhydachevskii, Ya. A.; Ubizskii, S. B.; Suchocki, A.; Scientific Research Company “Carat”, Lviv, Ukraine; Ivan Franko National University of Lviv, Ukraine; Lviv Polytechnic National University, Ukraine; Institute of Physics, Polish Academy of Science, Warsaw, Poland; Institute of Physics, Kazimierz Wielki University, Bydgoszcz, Poland
Magnetically induced light scattering in Fe3O4 nanoparticle suspension
(Видавництво національного університету „Львівська політехніка”, 2009) Malynych, S. Z.; Ballato, John; Ubizskii, S. B.; Kornev, K.
Optical Properties of GGG Epitaxial Films Grown from PbO-B2O3-V2O5 Flux
(2017-05-29) Syvorotka, I. I.; Sugak, D. Yu.; Luchechko, A. P.; Zhydachevskii, Ya. A.; Ubizskii, S. B.; Scientific Research Company “Carat”, Lviv, Ukraine; Lviv Polytechnic National University, Lviv, Ukraine; Ivan Franko National University of Lviv, Lviv, Ukraine; Institute of Physics, Polish Academy of Sciences, Warsaw, Poland
Optimization of Q-switched microchip Nd3+:YAG/Cr4+:YAG lasers for range finder applications
(Видавництво національного університету „Львівська політехніка”, 2009) Buryy, O. A.; Izhnin, A. I.; Syvorotka, I. I.; Sugak, D. Yu.; Ubizskii, S. B.; Vakiv, M. M.
Pendulum like rotation magnetization reversal of anisotropic magnetic film
(Видавництво національного університету „Львівська політехніка”, 2009) Ubizskii, S. B.; Pavlyk, L. P.
Rotation magnetization reversal fluxgate excited by the voltage source
(Видавництво Львівської політехніки, 2010) Pavlyk, L. P.; Ubizskii, S. B.
Fluxgate with rotation magnetization reversal of the isotropic disk core under the harmonic voltage source excitation has been analysed and the model of the response on the measured field components has been developed. When the excitation frequency is a half of the excitation circuit resonance frequency, the fluxgate sensitivity increases quadratically with the frequency and can exceed the sensitivity of the current driven fluxgate.
Temporal and Spatial Characteristics of the Diffusion Processes in LiNbO3 Crystals Caused by Thermo-Chemical Treatment
(2017-05-29) Sugak, D. Yu.; Buryy, O. A.; Syvorotka, I. I.; Yakhnevych, U. V.; Becker, K.-D.; Ubizskii, S. B.; Semiconductor electronics department, Lviv Polytechnic National University, Lviv, Ukraine; Scientific Research Company “Carat”, Lviv, Ukraine; Technical University Braunschweig, Braunschweig, Germany
The influence of the thermo-chemical treatment on the optical properties of YAG:Cr,Mg and GGG:Cr,Mg epitaxial films
(Видавництво Львівської політехніки, 2014) Buryy, О. А.; Ubizskii, S. B.; Syvorotka, I. I.; Shi., J.; Becker, K.-D.
The optical absorption spectra of YAG:Cr,Mg and GGG:Cr,Mg films are studied at in-situ conditions during high-temperature annealing in oxidizing and reducing atmospheres. The absorption spectra were measured in the range from 250 to 1500 nm at temperatures up to 1190 оС and the kinetics of absorption changes are registered at the wavelength of 450 nm. As it is shown, the oxidation of YAG:Cr,Mg films grown at low growth rates leads to increasing of the absorption in the visible region that caused by recharging of chromium ions, whereas the reduction of YAG:Cr,Mg films leads to the backward process. On the contrary, the reduction of GGG:Cr,Mg films increases their absorption, at that the kinetics of reduction has got the complicate, non-monotonous character. At sufficiently low temperatures (~ 800 оС) the oxidation leads to the opposite changes of the spectra of GGG:Cr,Mg films, however, at higher temperatures the changes of gas environment do not cause the noticeable changes of the spectra and the absorption remains at the sufficiently high level. The YAG:Cr,Mg film grown at higher growth rate demonstrates the behavior analogous to the one of GGG:Cr,Mg. Спектри оптичного поглинання плівок YAG:Cr,Mg та GGG:Cr,Mg досліджувалися в режимі insitu при високотемпературних відпалах в окисній та відновній атмосферах. Спектри поглинання вимірювалися в інтервалі від 250 до 1500 нм за температур до 1190оС, кінетичні криві зміни оптичної густиним реєструвалися на довжині хвилі 450 нм. Показано, що окислення плівок YAG:Cr,Mg, вирощених за нижчих швидкостей, веде до зростання оптичної густини у видимій області, що обумовлено поглинанням іонами хрому, тоді як відновлення плівок YAG:Cr,Mg веде до протилежного процесу. Навпаки, відновлення плівок GGG:Cr,Mg веде до зростання поглинання в цій області, при цьому кінетична крива зміни оптичної густини має складний, немонотонний характер. За істотно нижчих температур (~ 800оС) окислення веде до протилежних змін у спектрах поглинання плівок GGG:Cr,Mg, проте при вищих температурах зміна атмосфери відпалу не веде до помітних змін спектра і поглинання фіксується на достатньо високому рівні. Плівка YAG:Cr,Mg, синтезована при більшій швидкості, демонструє при відпалах поведінку, аналогічну до поведінки плівок GGG:Cr,Mg.
Thermal Behaviour of PrCo1–xFexO3 Probed by X-Ray Synchrotron Powder Diffraction and Impedance Spectroscopy Measurements
(2017-05-29) Pekinchak, O.; Sugak, D. Yu.; Ubizskii, S. B.; Suhak, Yu.; Fritze, H.; Vasylechko, L.; Lviv Polytechnic National University, Lviv, Ukraine; Institute of Energy Research and Physical Technologies, Clausthal University of Technology, Goslar, Germany
Thick epitaxial YIG films with narrow FMR linewidth
(Видавництво Львівської політехніки, 2012) Syvorotka, I. I.; Syvorotka, I. M.; Ubizskii, S. B.
The La-doped yttrium iron garnet (YIG) films with thickness up to 130 μm were grown by liquid phase epitaxy (LPE) method. All grown thick films demonstrate “mirror” and “striation” types of surface morphology that depend from film growth temperature and thickness. Addition of B2O3 is favourable to a change the surface morphology into a “mirror” one. The mechanisms of the morphological changes are discussed. It was found that the ferromagnetic resonance (FMR) linewidth appreciably depends from surface morphology of grown films. For thick films with “mirror” surface the FMR linewidth is less than 0.8 Oe and more than ten times less in comparison with films with “striation” surface.
Ytterbium ions recharging processes in Yb:Y3Al5O12 single crystals and films
(Видавництво національного університету “Львівська політехніка”, 2009) Martynyuk, N. V.; Buryy, O. A.; Ubizskii, S. B.; Syvorotka, I. I.; Börger, A.; Becker, K.-D.
Особливості кінетики радіаційного дефектоутворення за умови формування комплексів дефектів
(Видавництво Львівської політехніки, 2017-03-28) Бурий, О. А.; Убізський, С. Б.; Buryy, O.; Ubizskii, S. B.; Національний університет “Львівська політехніка”; Lviv Polytechnic National University
На основі розв’язку системи диференціальних рівнянь проаналізовано кінетику накопичення радіаційних дефектів у кристалічних середовищах за умови виникнення комплексів дефектів. Встановлено характерні особливості дозових залежностей, які відображають процес утворення комплексів дефектів.
Сенсори газів на наноструктурах: сучасний стан та перспективи досліджень
(Видавництво Львівської політехніки, 2017-03-28) Бурий, О. А.; Убізський, С. Б.; Buryy, O.; Ubizskii, S. B.; Національний університет “Львівська політехніка”; Lviv Polytechnic National University
Проаналізовано основні досягнення у галузі розроблення газових сенсорів резис- тивного типу, зокрема, створення нових наноархітектур, які дають змогу істотно покра- щити робочі характеристики сенсорів. Показано, що використання у таких структурах середовищ на основі нанокристалів перовськитів дасть можливість в перспективі забез- печити переваги над сенсорами на традиційних напівпровідникових оксидах металів.