Вісники та науково-технічні збірники, журнали
Permanent URI for this communityhttps://ena.lpnu.ua/handle/ntb/12
Browse
2 results
Search Results
Item Structural, thermal and electrical properties of doped poly(3,4-ethylenedioxythiophene)(Publishing House of Lviv Polytechnic National University, 2016) Kelkar, Deepali; Chourasia, AshishPoly(3,4-ethylenedioxythiophene) (PEDOT) was chemically synthesized, undoped and then re-doped using FeCl3 as well as camphorsulfonic acid (CSA). FTIR results confirm the nature of the synthesized and doped samples. XRD analysis indicates crystal structure modification after doping and was also used to calculate crystallinity of samples. Crystallinity increases after FeCl3 doping, whereas it reduces due to CSA doping. TGADTA results show reduction in Tg value for FeCl3 doped sample while it increases for CSA doped samples compared to that of undoped PEDOT. Reduction in Tg indicates plasticizing effect of FeCl3 whereas increase in Tg show anti-plasticizing effect of CSA in PEDOT. Conductivity (s) value increases by two orders of magnitude after doping. Logs vs. 1/T graph show metallic nature of undoped PEDOT above 308 K, however both doped samples show semiconducting nature from 301 to 383 K. Хімічно синтезовано недопований і допований за допомогою FeCl3 і камфор сульфокислоти (КСК) полі(3,4-етилендіоксітіофен) (ПЕДОТ). За допомогою Фур’є-спектроскопії підтверджено природу синтезованого і допованого зразків. За допомогою дифракції рентгенівських променів встановлено кристалічну структуру після допування і розрахована кристалічність зразків. Показано, що кристалічність збільшується після допування FeCl3, але знижується при допуванні КСК. За результатами ТГА-ДТА встановлено, що значення температури силування (Tg) для зразка, допованого FeCl3, знижується, а для зразка, допованого КСК – збільшується, у порівнянні з недопованим ПЕДОТ. Зниження Tg вказує на пластифікуючий ефект FeCl3, тоді як збільшення Tg – на антипластифікуючий ефект КСК в ПЕДОТ. Визначено, що після допування значення електропровідності (s) збільшується на два порядки. Залежність logs–1/T вказує на металічну природу недопованого ПЕДОТ за температури вище 308 К, і напівпровідникову природу обох допованих зразків в інтервалі 301–383 К.Item Structural properties of polythiophene doped with FeCl3(Publishing House of Lviv Polytechnic National University, 2011) Kelkar, Deepali; Chourasia, AshishPolythiophene is chemically synthesized and doped with FeCl3 for 2.5, 5 and 10 h. For structural investigation all samples have been characterized using different techniques. The results of elemental analysis show that with the increase of doping duration the Fe content increases while the S content decreases. FTIR spectrum reveals the complex formation between FeCl3 and polythiophene. UV-Visible results have been used to calculate band gap energy. Analysis of XRD shows that after polythiophene doping by FeCl3 some modifications in crystal structure and increase in crystallinity take place. Morphological studies using SEM have been carried out. TGA-DTA results indicate the reduction in Tg values with the increase in dopant concentration as well as increase in thermal stability due to doping. Проведено синтез політіофену, промотованого FeCl3 протягом 2,5, 5 і 10 год. Для структурних досліджень використовувались різні методики. За результатами елементного аналізу встановлено, що зі збільшенням часу промотування вміст заліза збільшується, а вміст сірки зменшується. Фур'є-спектроскопія підтверджує утворення комплексу між FeCl3 і політіофеном. Спектрофотометричний аналіз використано для розрахунку енергії забороненої зони. Встановлено, що після промотування політіофену FeCl3 відбуваються деякі зміни в кристалічній структурі полімеру та зростає його кристалічність. Морфологічні дослідження проведені з використанням СЕМ. Результати термогравиметричного аналізу свідчать про зменшення значення температури склування зі збільшенням концентрації промотора, а також про збільшення термічної стабільності.