    Some properties of elastomeric compositions with high-dispersed carbon additives
    (Publishing House of Lviv Polytechnic National University, 2016) Vishnevskii, Konstantin; Shashok, Zhanna; Prokopchuk, Nikolai
    The influence of a carbon nanomaterial obtained in a high-voltage discharge plasma on the endurance of elastomer compositions has been investigated. Complex tests of elastomeric compositions with highly dispersed carbon additives allowed us to confirm the model of nonlinear elastic deformation of macromolecules and adhesion between the elastomer and the nanoparticles. The results of these investigations agree with those obtained in determining the Mooney viscosity and relaxation, the parameters of the vulcanization kinetics of rubber mix, conventional tensile strength, and relative breaking elongation of highly filled rubbers based on butadiene-nitrile caoutchoucs. To verify the assumed mechanism underlying the action of a carbon nanomaterial on elastomer compositions, the parameters of their vulcanizing network have been determined using the method of equilibrium swelling. Досліджено вплив вуглецевого наноматеріалу, отриманого в плазмі високовольтного розряду, на довговічність еластомерних композицій. Комплексними дослідженнями еластомерних композицій підтверджено модель нелінійної пружної деформації макромолекул, а також адгезійну взаємодію між еластомером і наночастинками. Результати досліджень узгоджуються з даними, отриманими при визначенні в‘язкості за Муні, релаксації та кінетиці вулканізації гумових сумішей, умовної міцності при розтягненні та відносному видовженні при розриві високонаповнених гум на основі бутадієннітрильних каучуків. Для підтвердження передбачуваного механізму, який лежить в основі впливу вуглецевого наноматеріалу на еластомерні композиції, параметри вулканізаційної сітки визначені методом рівноважного набухання.
  • Thumbnail Image
    Item
    Synthesis and characterization of polyaniline nanofibres by rapid liquid-liquid interfacial polymerization method
    (Publishing House of Lviv Polytechnic National University, 2011) Kulkarni, Milind; Kale, Bharat; Apte, Sanjay; Naik, Sonali; Mulik, Uttam; Amalnerkar, Dinesh
    Inherently conducting polymer polyaniline (Pani) has been synthesized by a novel interfacial polymerization technique using trichloroethane as organic media. Ammonium peroxydisulphate was used as an oxidizing agent dissolved in aqueous media. The synthesized polymer was subjected to the physico-chemical characterization by UV-Vis and FT-IR Spectroscopy and Scanning Electron Microscopy. From the SEM Micrographs it was observed that interfacial polymerization offers the fibrillar type of morphology having 200 nm sized fibers. Thermal properties of the synthesized polyaniline nanofibres were evaluated by thermogravimetric analysis. Conductivity of the polymer was measured by four-probe conductivity measurement technique and found to be ~ 0.1 S/cm. Сучасним методом міжфазної полімеризації з використанням трихлоретану як органічного середовища синтезовано інтенсивно провідний полімер поліаніліну (ПАНІ). Як окисник використано водний розчин пероксидисульфату амонію. Синтезований полімер охарактеизовано з викорис танням методу спектрофотометричного аналізу, Фур’є спектроскопією та скануючою електронною мікроскопією. Знайдено, що міжфазна полімеризація приводить до морфології фібрилярного типу з розміром волокон 200 нм. Оцінювання термічних властивостей синтезованих нановолокон поліаніліну проведено з використанням термогравіметричного аналізу. Провідність полімеру вимірювалася за допомогою методики чотирьох-електродної провідності і становила ~ 0,1 См/см.