Електронний архів Науково-технічної бібліотеки
Permanent URI for this communityhttps://ena.lpnu.ua/handle/ntb/2
Browse
4 results
Search Results
Item Modified phenol-formaldehyde resins and their application in bitumen-polymeric mixtures(Publishing House of Lviv Polytechnic National University, 2013) Strap, Galyna; Astakhova, Olena; Lazorko, Olexander; Shyshchak, Oleh; Bratychak, MichaelPhenol-formaldehyde resins (PhFR) with reactive methacrylate fragments or labile peroxy bonds in the side branches used as a polymeric component of bitumen-polymeric mixtures have been investigated. Taking into account that PhFR with peroxy fragments based on epoxy resin does not described in literature, its synthesis procedure has been developed. The kinetic regularities of the reaction between peroxy derivative of epoxy resin (PDER) and phenol group of PhFR were studied taking the reaction of PDER with phenol as an example. The structure of PhFR with peroxy groups (PhFRP) has been confirmed by IR-studies. Bitumenpolymeric mixtures with PhFRP or PhFR with unsaturated fragments (PhFRU) in the amount of 1, 3, 5 or 7 mass parts per 100 g of petroleum bitumen were examined at 443, 463 or 483 K for 0.5, 1.0 or 2.0 h. The composition of bitumn-polymeric mixtures has been determined using the group analysis. Вивчена можливість використання як полімерного компоненту бітум-полімерних сумішей фенол-формальдегідних смол (ФФС), які містять у бічних відгалуженнях реакційноздатні метакрилатні фрагменти або лабільні пероксидні зв’язки. Враховуючи те, щоФФСз пероксидними фрагментами на основі епоксидної смоли в літературі не описана, розроблена методика її синтезу. Кінетичні закономірності реакції між пероксидною похідною епоксидної смоли (ППЕС) і фенольною групою ФФС вивчені на прикладі ППЕС з фенолом. Структура ФФС з пероксидними групами (ФФСП) підтверджена ІЧ- спектроскопічними дослідженнями. Бітум-полімерні суміші, що містили ФФСП або фенол-формальдегідну смолу з ненасиченими фрагментами (ФФСН) в кількості 1, 3, 5 чи 7 мас.част. на 100 г нафтового бітуму вивчені за температур 443, 463 або 483 К впродовж 0,5, 1,0 чи 2,0 год. З використанням структурно-групового методу аналізу встановлено склад бітум-полімерних сумішей.Item Modified phenol-formaldehyde resins and their application in bitumen-polymeric mixtures(Publishing House of Lviv Polytechnic National University, 2013) Strap, Galyna; Astakhova, Olena; Lazorko, Olexander; Shyshchak, Oleh; Bratychak, MichaelPhenol-formaldehyde resins (PhFR) with reactive methacrylate fragments or labile peroxy bonds in the side branches used as a polymeric component of bitumen-polymeric mixtures have been investigated.Taking into account that PhFR with peroxy fragments based on epoxy resin does not described in literature,its synthesis procedure has been developed. The kinetic regularities of the reaction between peroxy derivative of epoxy resin (PDER) and phenol group of PhFR were studied taking the reaction of PDER with phenol as an example. The structure of PhFR with peroxy groups (PhFRP) has been confirmed by IR-studies. Bitumenpolymeric mixtures with PhFRP or PhFR with unsaturated fragments (PhFRU) in the amount of 1, 3, 5 or 7 mass parts per 100 g of petroleum bitumen were examined at 443, 463 or 483 K for 0.5, 1.0 or 2.0 h. The composition of bitumn-polymeric mixtures has been determined using the group analysis. Вивчена можливість використання як полімерного компоненту бітум-полімерних сумішей фенол-формальдегідних смол (ФФС), які містять у бічних відгалуженнях реак- ційноздатні метакрилатні фрагменти або лабільні пероксидні зв’язки. Враховуючи те, що ФФСз пероксидними фрагментами на основі епоксидної смоли в літературі не описана, розроблена методика її синтезу. Кінетичні закономірності реакції між пероксидною похідною епоксидної смоли (ППЕС) і фенольною групою ФФС вивчені на прикладі ППЕС з фенолом. Структура ФФС з пероксидними групами (ФФСП) підтверджена ІЧ-спектроскопічними дослідженнями. Бітум-полімерні суміші,що містили ФФСП або фенол-формальдегідну смолу з ненасиченими фрагментами (ФФСН) в кількості 1, 3, 5 чи 7 мас.част. на 100 г нафтового бітуму вивчені за температур 443, 463 або 483 Кв продовж 0,5, 1,0 чи 2,0 год. З використанням структурно-групового методу аналізу встановлено склад бітум-полімерних сумішей.Item Phenol-formaldehyde resins of novolac type with unsaturated side bonds(Publishing House of Lviv Polytechnic National University, 2013) Bratychak, Michael; Strap, Galyna; Astakhova, Olena; Shyshchak, OlenaThe reaction between novolac phenolformaldehyde resin and glycidylmethacrylate has been studied in the presence of potassium hydroxide and the synthesis procedure of phenol-formaldehyde resin with unsaturated side bonds has been suggested. The effective rates and activation energy of the mentioned reaction have been calculated. The structure of synthesized resin was confirmed by IR-spectroscopy. The synthesized resin may be used as active component of polymeric blends based on ED-20 industrial epoxy resin, its peroxy derivative (PO) and TGM-3 oligoesteracrylate. The process was controlled by gel-fraction content and polymeric films hardness. Physico-mechanical and protective properties of the synthesized epoxy-oligoesteric mixtures have been studied. Вивчена, в присутності гідроксиду калію, реакція взаємодії новолачної феноло-формальдегідної смоли з гліцидилметакрилатом та запропонована методика синтезу феноло-формальдегідної смоли, яка містить бічні ненасичені зв’язки. Розраховані ефективні швидкості та енергія активації такої реакції. Структура синтезованої смоли підтверджена ІЧ- спектроскопічними методами дослідження. Показана можливість використання такої смоли як активного компоненту полімерних сумішей на основі промислової епоксидної смоли ЕД-20, її пероксидної похідної (ПО) та олігоестеракрилату ТГМ-3. Контроль за процесами структурування проводили внаслідок визначення вмісту гель-фракції та твердості полімерних плівок. Вивчені фізико-механічні та захисні властивості структурованих епокси-олігоестерних сумішей.Item Chemical modification of ED-24 epoxy resin by adipic acid(Publishing House of Lviv Polytechnic National University, 2012) Bratychak, Micael; Astakhova, Olena; Mykhailiv, Olena; Stryzhachuk, Alina; Shyshchak, OlenaThe possibility of epoxy resin carboxyontaining derivative (CDER) obtaining has been studied on the basis of dianic epoxy resin ED-24 and adipic acid (AA). The synthesized CDER contains epoxy and carboxy groups at the same time. Used catalysts were benzyltriethylammonium chloride (BTEACh); 1,4-diazobicyclo[2,2,2] octane; N,N-dimethylaminopyridine; 18-Crown-6, potassium hydroxide, triethylamine and 18-Crown-6+ZnCl2 catalytic system. The effect of the catalyst nature and amount, reagents ratio, process temperature and time on the reaction proceeding between ED-24 and AA has been determined. The structure of CDER synthesized in the presence of BTEACh and its characterics were confirmed by IR-spectroscopy. Using industrial dianic epoxy resin ED-20 the cross-linking of polymeric composites containing 10, 20 and 30 mass parts of CDER has been investigated at 413 K in the presence of polyethylenepolyamine. Вивчена можливість одержання на основі діанової епоксидної смоли ЕД-24 і адипінової кислоти (АК) карбоксилвмісної похідної епоксидної смоли (КПЕС), яка одночасно містить вільну епоксидну і карбоксильну групу. Встановлено вплив природи та кількості каталізатора, зокрема бензилтриетиламонію хлористого (БТЕАХ), 1,4-діазобіцикло[2,2,2]октану, N,N-диметиламінопіридину, 18-Краун-6, гідроксиду калію, триетиламіну та каталітичної системи 18-Краун-6+ZnCl2, співвідношення реагуючих речовин, температури і тривалості реакції на протікання реакції між ЕД-24 та АК. КПЕС синтезована в присутності як каталізатор БТЕАХ та охарактеризована. ІЧ-спектроскопічними дослідженнями підтверджена структура КПЕС. З використанням промислової діанової епоксидної смоли ЕД-20 вивчено при 413 К структурування у присутності поліетиленполіаміну полімерних сумішей, що містять 10, 20 і 30 мас.част. КПЕС.