Defect structure of zirconium oxide nanosized powders with Y2O3, Sc2O3, Cr2O3 impurities
Loading...
Date
2012
Journal Title
Journal ISSN
Volume Title
Publisher
Видавництво Львівської політехніки
Abstract
Formation mechanisms of paramagnetic centers originating from Zr3+ and Cr3+ ions as well as the influence of composition of nanoparticles on thermogeneration processes of these paramagnetic centers in ZrO2 structure were studied. A set of nanosized powders of zirconium oxide was investigated by electron paramagnetic resonance method: nominally pure ZrO2; ZrO2 with Y2O3 and Sc2O3; ZrO2 with Cr2O3; ZrO2 with Y2O3 and Cr2O3. It is observed that the influence of annealing on EPR lines of Zr3+ and Cr3+ions is different. Nuclear magnetic resonance data have shown that zirconium dioxide nanoparticles with Sc and Y impurities include two types of water molecules and two types of hydroxyl groups.
Description
Keywords
nanosized powder, defects, impurities, electron paramagnetic resonance, nuclear magnetic resonance
Citation
Defect structure of zirconium oxide nanosized powders with Y2O3, Sc2O3, Cr2O3 impurities / L. Yurchenko, I. Bykov, A. Vasylyev, V. Vereshchak, G. Suchaneck, L. Jastrabik, A. Dejneka // Оксидні матеріали електронної техніки – отримання, властивості, застосування (ОМЕЕ – 2012) : збірник матеріалів міжнародної наукової конференції, 3-7 вересня 2012 року, Львів, Україна / Національний університет “Львівська політехніка”. – Львів : Видавництво Львівської політехніки, 2012. – С. 114–115. – Bibliography: 6 titles.