Thick epitaxial YIG films with narrow FMR linewidth
Loading...
Date
2012
Journal Title
Journal ISSN
Volume Title
Publisher
Видавництво Львівської політехніки
Abstract
The La-doped yttrium iron garnet (YIG) films with thickness up to 130 μm were grown by liquid phase epitaxy (LPE) method. All grown thick films demonstrate “mirror” and “striation” types of surface morphology that depend from film growth temperature and thickness. Addition of B2O3 is favourable to a change the surface morphology into a “mirror” one. The mechanisms of the morphological changes are discussed. It was found that the ferromagnetic resonance (FMR) linewidth appreciably depends from surface morphology of grown films. For thick films with “mirror” surface the FMR linewidth is less than 0.8 Oe and more than ten times less in comparison with films
with “striation” surface.
Description
Keywords
liquid phase epitaxy, yttrium iron garnet films, surface morphology, ferromagnetic resonance linewidth
Citation
Syvorotka I. I. Thick epitaxial YIG films with narrow FMR linewidth / I. I. Syvorotka, I. M. Syvorotka, S. B. Ubizskii // Оксидні матеріали електронної техніки – отримання, властивості, застосування (ОМЕЕ – 2012) : збірник матеріалів міжнародної наукової конференції, 3-7 вересня 2012 року, Львів, Україна / Національний університет “Львівська політехніка”. – Львів : Видавництво Львівської політехніки, 2012. – С. 264–265. – Bibliography: 5 titles.