Structural and magnetic characterization of functional surface coated maghemite nanoparticles
Loading...
Date
2012
Journal Title
Journal ISSN
Volume Title
Publisher
Видавництво Львівської політехніки
Abstract
Nanoparticles composed of magnetic γ-Fe2O3 core and organic shell were synthesized via template synthesis in the presence of functional oligoperoxide surfactants and further graft-polymerization initiated from their surface. X-ray diffraction (XRD), transmission electron microscopy (TEM) and magnetic measurements (PPMS) were used to characterize the obtained magnetic system of core-shell nanoparticles. XRD results confirm the existence of γ-Fe2O3 phase as well as show an average diameter of nanoparticles around 10 nm. The obtained particles are superparamagnetic at the room temperature. Magnetic measurements indicate also sufficiently strong dipolar interparticle interactions at low temperatures.
Description
Keywords
core-shell γ-Fe2O3 nanoparticles, dipolar interparticle interactions
Citation
Structural and magnetic characterization of functional surface coated maghemite nanoparticles / P. Demchenko, N. Mitina, A. Zaichenko, N. Nedelko, S. Lewińska, A. Ślawska-Waniewska, P. Dłużewski, M. Bilska, S. Ubizskii // Оксидні матеріали електронної техніки – отримання, властивості, застосування (ОМЕЕ – 2012) : збірник матеріалів міжнародної наукової конференції, 3-7 вересня 2012 року, Львів, Україна / Національний університет “Львівська політехніка”. – Львів : Видавництво Львівської політехніки, 2012. – С. 268–269. – Bibliography: 4 titles.