Organic synthesis and characterization of electrically conducting poly(o-toluidine) doped with organic acid

Abstract

Poly(o-toluidine) doped with acrylic acid and without it was synthesized by using chemical oxidative polymerization technique. With the help of this method the polymer, poly(o-toluidine) was synthesized in the form of emeraldine salt. The oxidizing agent used for this method is the ammonium persulphate .The polymer products were characterized by UV-Visible and FTIR spectroscopy. The polymer, poly(o-toluidine) doped with acrylic acid was highly soluble in common organic solvents like m-cresol, NMP, DMF etc. The FTIR studies demonstrate that the acrylic acid doped poly(o-toluidine) shows broad and intense band at 3250–3000 cm-1 and 1160–1100 cm-1 account for the higher degree of doping. These results are well supported by conductivity measurements. Методом хімічної оксидаційної полімеризації синтезовано полі(о-толуїдин) з додатками акрилової кислоти і без неї у формі емералдіновой солі. Як окисник використано персульфат амонію. З використанням УФ- та Фур'є-спектpоскопії визначено характеристики продукту. Показано, що полі(о-толуїдин) з додатками акрилової кислоти добре розчиняється у таких відомих органічних розчинниках як м-крезол, НМП, ДМФ тощо. Фур’є-спектроскопічними дослідженнями встановлено, що полі(о-толуїдин) з додатками акрилової кислоти має широку та інтенсивну смугу при 3250–3000 см 1 і смугу при 1160–1100 см 1 при більшій кількості додатків. Результати підтверджені вимірюванням провідності.