Cross-linking of epoxy-oligoesteric mixtures in the presence of carboxy-containing derivative of ED-24 epoxy resin
No Thumbnail Available
Date
2013
Journal Title
Journal ISSN
Volume Title
Publisher
Lviv Polytechnic Publishing House
Abstract
Cross-linking of epoxy-oligomeric mixtures has been studied at room temperature and at heating to 383,403 and 423 K for 15, 30, 45, 60 and 75 min in the presence of polyethylenepolyamine. The mixtures consist of industrial ED-20 epoxy resin,oligoesteracrylate TGM-3 and carboxy-containing derivative of ED-24. The effect of mixture composition, temperature and process time on the gel-fraction content and hardness of polymeric films has been examined. Using IR-spectroscopy the chemism of network formation has been determined. Вивчено структурування за кімнатної температури і при нагріванні до 383, 403 або 423 К впродовж 15, 30, 45, 60 і 75 хв. епокси-олігоестерних сумішей, що складаються з промислової епоксидної смоли ЕД-20,олігоестеракрилату ТГМ-3 і карбоксилвмісної похідної епоксидної смоли ЕД-24 (КПЕС) в присутності поліетиленполіаміну. Встановлено вплив складу суміші, температури і тривалості
структурування на вміст гель-фракції в зразках та твердість полімерних плівок. З використанням ІЧ спектроскопії встановлено хімізм утворення просторовозшитих структур.
Description
Keywords
epoxy resin, oligoesteracrylate, carboxy group, IR-spectroscopy, acid number, cross-linking, cross-linking, film hardness, епоксидна смола, олігоестеракрилат, карбоксильна група, кислотне число, структурування, ІЧ спектроскопія, гель-фракція, твердість плівок
Citation
Cross-linking of epoxy-oligoesteric mixtures in the presence of carboxy-containing derivative of ED-24 epoxy resin / Michael Bratychak, Bogdana Bashta, Piotr Bruzdziak, Olena Astakhova, Olena Shyshchak // Chemistry & Chemical Technology. – 2013. – Volume 7, number 1. – P. 41–46. – Bibliography: 7 titles.