Comparative studies on physico-chemical properties of indium sulfide films deposited under different deposition conditions by chemical bath deposition

Abstract

Indium sulfide films have been deposited using chemical bath deposition onto glass and indium tin oxide (ITO) coated glass substrates. The influences of different deposition parameters viz. substrate and pH have been studied. The films were characterized by different techniques with respect to their crystal structure, surface morphology and compositional property by means of X-ray diffraction, scanning electron microscopy, energy dispersive spectroscopy and optical absorption. X-ray diffraction studies revealed amorphous nature of the films. The scanning electron microscopy of deposited indium sulfide film on ITO coated glass substrate shows random orientation of grains where as those on glass substrates show dumbbell shape. Optical absorption study revealed that band gap varies from 2.29 to 2.79 eV for the deposited film. Сульфідні плівки індію хімічно осаджені на скло та скло, покрите індій-олово оксидом (ITO). Вивчено вплив різних параметрів осадження, а саме вплив природи підкладки і рН середовища. Кристалічну будову, морфологію поверхні і складу отриманих плівок охарактеризовано за допомогою рентгенівської дифракції, скануючої електронної мікроскопії, енергодисперсійної спектроскопії та оптичної абсорбції. Аморфний характер плівок підтверджений рентгенівськими дослідженнями. З використанням скануючої електронної мікроскопії доведено випадкову орієнтацію осаджених індій-сульфідних плівок на ІТО-склі, тоді як плівки, осаджені на скляні підкладки, мають форму гантелей. Дослідження оптичного поглинання показало, що для висадженої плівки ширина забороненої зони змінюється від 2,29 до 2,79 еВ.