Development and characterization of novel fore safe epoxy resins

Abstract

The curing system for newly developed solid state fire safe epoxy resins using dicyandiamide (DICY) was introduced. Composites of epoxy resins obtained from diglycidyl ether of 1,1-dichloro-2,2bis(4-hydroxyphenyl)ethylenebisphenol-C(BPC)andbisphenol- A (BPA) epoxy resins in the reaction with BPC and BPA and DICY hardener were studied. Solid epoxy resins were synthesised by the use of two different heating methods: conventional and microwave reactor. The quantities of DICY additions were 0.5–5.0%, optimum was found to be 3%. Limited oxygen index(OI)tests for different epoxy resins and addition of flame–retardants were carried out. The highest value of OI was 34.6. As additional flame-retardants were used zinc stannates(ZS,ZHS). Evident OI increase was noted from 27.0 for classical epoxies, 34.6 for BPC cured epoxies and 44 for cured composites with the addition of Zn/Sn flame-etardants. Розглянуто затверджену систему нових пожежно-безпечних твердих епоксидних смол синтезованих з використанням дициандіаміду (ДЦДА). Композити епоксидних смол одержані з игліциділовогоетеру 1,1-дихлор-2,2 біс(4- гідроксифеніл)етилену бісфенолу С (БФС) і епоксидних смол бісфенолу А (БФА) за реакцією між БФС і БФА з використанням як затвердника ДЦДА. Тверді епоксидні смоли синтезовані з використанням двох різних методів нагріву: звичайного і у мікрохвильовому реакторі. Кількість ДЦДА коливалась від 0,5 до 5,0%. Визначено оптимальну концентрацію затвердника, яка становила 3%. Визначено кисневий індекс (КІ) для різних епоксидних смол. Найвищий КІ становив 34,6. Як додаткові сповільнювачі полум’я використовували станати цинку. Показано зростання КІ з 27,0 для класичних епоксидів до 34,6 для затверджених епоксидів і до 44 для затверджених композитів з додатком Zn/Sn сповільнювачів.