Influence of zirconium hydrophosphate nanoparticles on porous structure and sorption capacity of the composites based on ion exchange resin
No Thumbnail Available
Date
2016
Journal Title
Journal ISSN
Volume Title
Publisher
Publishing House of Lviv Polytechnic National University
Abstract
Evolution of swelling of gel-like strongly acidic resin and organic-inorganic composites based on this ionexchanger was investigated. Non-aggregated nanoparticles of zirconium hydrophosphate were found to provide size invariability of the polymer pores, which contain functional groups (up to 20 nm), the nanoparticle aggregates squeeze these pores (down to 3 nm). Owing to this, the nanocomposite shows higher break-through capacity during removal of Ni2+ from water, than the sample modified only with aggregates. Досліджено еволюцію набухання гелевої сильнокислотної смоли та органо-неорганічних композитів на її основі. Знайдено, що неагреговані наночастинки гідрофосфату цирконію, інкорпоровані до полімеру, забезпечують незмінність розміру його пор, які містять функціональні групи (до 20 нм), а агрегати наночастинок здавлюють ці пори (до 3 нм). Зважаючи на це, нанокомпозит демонструє більш високу здатність до проскоку при вилученні йонів Ni2+ з води, ніж зразок, модифікований тільки агрегатами.
Description
Keywords
organic-inorganic ion exchangers, nanoparticles, zirconium hydrophosphate, polymer porosity, standard contact porosimetry, органо-неорганічні йоніти, наночастинки, гідрофосфат цирконію, пористість полімеру, еталонна контактна порометрія
Citation
Influence of zirconium hydrophosphate nanoparticles on porous structure and sorption capacity of the composites based on ion exchange resin / Yuliya Dzyazko, Ludmila Ponomarova, Yurii Volfkovich, Valentina Tsirina, Valentin Sosenkin, Nadiya Nikolska, Volodimir Belyakov // Chemistry & Chemical Technology. – 2016. – Volume 10, number 3. – P. 329–335. – Bibliography: 15 titles.