Synthesis and characterization of polyaniline nanofibres by rapid liquid-liquid interfacial polymerization method

Abstract

Inherently conducting polymer polyaniline (Pani) has been synthesized by a novel interfacial polymerization technique using trichloroethane as organic media. Ammonium peroxydisulphate was used as an oxidizing agent dissolved in aqueous media. The synthesized polymer was subjected to the physico-chemical characterization by UV-Vis and FT-IR Spectroscopy and Scanning Electron Microscopy. From the SEM Micrographs it was observed that interfacial polymerization offers the fibrillar type of morphology having 200 nm sized fibers. Thermal properties of the synthesized polyaniline nanofibres were evaluated by thermogravimetric analysis. Conductivity of the polymer was measured by four-probe conductivity measurement technique and found to be ~ 0.1 S/cm. Сучасним методом міжфазної полімеризації з використанням трихлоретану як органічного середовища синтезовано інтенсивно провідний полімер поліаніліну (ПАНІ). Як окисник використано водний розчин пероксидисульфату амонію. Синтезований полімер охарактеизовано з викорис танням методу спектрофотометричного аналізу, Фур’є спектроскопією та скануючою електронною мікроскопією. Знайдено, що міжфазна полімеризація приводить до морфології фібрилярного типу з розміром волокон 200 нм. Оцінювання термічних властивостей синтезованих нановолокон поліаніліну проведено з використанням термогравіметричного аналізу. Провідність полімеру вимірювалася за допомогою методики чотирьох-електродної провідності і становила ~ 0,1 См/см.