Chemistry & Chemical Technology. – 2009. – Vol. 3, No. 2

Permanent URI for this collectionhttps://ena.lpnu.ua/handle/ntb/2088

The scientific-technical journal

It is the scientific-technical journal in English in Ukraine discussing actual problems of chemistry and chemical technology. Compared with other chemical journals Ch&ChT is publishing materials of both theoretical and practical values in such fields as analytical, general organic, physical and inorganic chemistry; chemistry of high molecular compounds; materials science and engineering; chemical kinetics and catalysis; technology of inorganic substances; technology of organic synthesis products; chemical technology of processing of combustible minerals; processes and apparatus of chemical and food productions; biotechnology and ecology.

Chemistry & Chemical Technology : [the scientific-technical journal] / Lviv Polytechnic National University ; editor-in-chief M. Bratychak. – Lviv : Publishing House of Lviv Polytechnic National University, 2009. – Volume 3, number 2. – P. 82–168, VI : ill.

Browse

Subject: search.filters.subject.механічні властивості

Search Results

Now showing 1 - 1 of 1
  • Thumbnail Image
    Item
    Preparation and properties of (epoxy resin)/(nylon 6,6 oligomer) blends
    (Publishing House of Lviv Polytechnic National University, 2009) Bragg, Jason; Alvarez-Castillo, Alberto; Trejo-Duran, Monica; Castano, Victor
    A series of polymer alloys based on different compositions of Nylon 6,6 oligomers (NYL66Oґs) and epoxy resin have been prepared. The oligomer was extracted from the waste residues of the industrial production of nylon 6,6 and was dissolved in the epoxy resin. The mixture was crosslinked at 333 K using dodecenylsuccinic anhydre (DDSA) as a curing agent. The tensile strength and flexural modulus were found to increase with the addition of NYLO66O up to a maximum value of 2 wt % oligomer content. Both, the tensile and impact strength show a maximum increase due to the addition of 35 wt%NYLO66O. The compressive strength testing revealed a considerable increase, up to 87 %, over that of the neat epoxy with the addition of 1 wt % NYLO66O. An interesting relationship between the mechanical properties and the developed morphology of the blends has been found. Вивчено низку полімерних сумішей на основі різних складів епоксидна смола/олігомери Найлон 6,6. Отримані екстакцією з відпадів промислового виробництва Найлону 6.6 олігомери розчиняли в епоксидній смолі і зшивали при 333 К з використанням додеценілянтарного ангідриду. Знайдено, що міцність до розривання та модуль згинання зростають із додаванням до 2% мас. Найлону. Введення у суміш 35% мас. Найлону підвищує міцність до розривання та ударну в'язкість. Наведені порівняльні тести для чистої епоксидної смоли і сумішей з додаванням Нейлону. Встановлена залежність між механічними властивостями та морфологією сумішей.