Impact of conducting polymer filler on the dielectric properties of Nylon 11

Abstract

The dielectric studies of semi-crystalline Nylon 11 filled with a conducting polymer (PANI) were investigated in a wide range of frequency and temperature by using Impedance Analyzer. The main focus was on the effects of conducting filler content on dielectric properties of Nylon 11. The prominent factors such as dielectric permittivity, loss factor, and loss tangent were studied at high frequency. Two different concentrations (1 % and 5 % w/w) of the conducting filler were used. It was observed that with the increase of fillers concentration, the value of dielectric permittivity (?’), the dissipation factor (?’’) and loss (tand ) decrease compared to pure Nylon 11. В широкому інтервалі частоті температур, з використанням імпедансного аналізатора, досліджено діелектричні властивості напівкристалічного Найлону 11, наповненого провідним полімером (ПАНІ). Головна увага була звернута на вплив концентрації провідного полімеру на діелектричні властивості Найлону 11. При високих частотах вивчали такі чинники, як діелектрична проникність, коефіцієнт втрат і тангенс кута діелектричних втрат. Досліджено дві різні концентрації наповнювача: 1 і 5 % мас. Визначено, що з підвищенням концентрації наповнювача величини діелектричної проникності, коефіцієнт розсіювання і тангенс кута втрат зменшуються порівняно з чистим Найлоном 11.