TPU/Mica composites prepared in torque rheometer: processability, mechanical properties and vorphology

Abstract

This work is concerned with the preparation of thermoplastic polyurethane elastomer (TPU) composites with mica, and their characterization as for processability, mechanical and thermal properties and morphology behavior. The amount of added mica varied from 0 to 20 phr and the results showed few interactions between mica and the polymer matrix. Processability is facilitated by the increasing amount of mica but TPU upon strain crystallizability, as well as Tg, decrease with the increase in mica content. The main interest in using mica is the evaluation of a low cost mineral as a reinforcing material for the engineering polymer TPU. Описаний процес підготовки композитів термопластичного поліуретанового еластомеру (ТПУ) з слюдою, та наведені такі їх характеристики, як технологічність, механічні та теплові властивості і морфологія. Кількість доданої слюди змінювалась від 0 до 20 мас.част. Показана взаємодія між слюдою і полімерною матрицею. Встановлено, що збільшення кількості слюди сприяє технологічності процесу, але при цьому зменшується напруження кристалізованості та температура склування. Показано, що низька вартість мінералу як укріплюю чого матеріалу для технічного полімеру ТПУ є критерієм оцінювання.