Technological features of forsterite containing powders synthesis

Abstract

Technological basics of forsterite powder synthesis by sol-gel method was developed. The expedience of use as a magnesium containing component of crystalline Mg(CH3COO)2∙4H2O due to the least duration of gel formation was shown. The temperature of the beginning of forsterite formation gel powder was determined by DTA and XRD methods (700 oС). The possibility of its reduction to 100 oС by introducing fluoride containing mineralizators was shown. The most effective is the use of a water-soluble mineralizator H2SiF6, it is confirmed by the presence of ekzo effects at lower temperatures. Technological parameters of monophasic forsterite powders obtention was established. The phase composition of the powder was done by the XRD method. The technological scheme of the forsterite obtention was shown. Розроблено технологічні основи синтезу форстеритового порошку золь-гель методом. Показано доцільність використання як магнійвмісного компонента кристалогідрату Mg(CH3COO)2∙4H2O через найменшу тривалість гелеутворення розчину. Методами ДТА і РФА встановлено температуру початку форстеритоутворення гель-порошків (700 oС). Показана можливість її зниження на 100 oС введенням флюорвмісних мінералізаторів. Найефективнішим є використання водорозчинного мінералізатора H2 SiF6, що підтверджується наявністю екзоефектів за нижчих температур. Встановлено технологічні параметри отримання монофазних порошків форстериту. Методом РФА встановлено фазовий склад порошку. Наведено технологічну схему отримання форстериту.