PbO2 based composite materials deposited from suspension electrolytes: electrosynthesis, physico-chemical and electrochemical properties

Abstract

Composite materials based on PbO2 containing TiO2 or ZrO2 were prepared from electrolytes containing a suspension of TiO2 or ZrO2. The contents of foreign oxides in the composite depend on the electrolyte composition and conditions of deposition. When a dispersed phase is incorporated into the composite coating, the dimensions of lead dioxide crystals decrease to submicro- and nano-size. Physico-chemical properties and electrocatalytic activity of composite materials are mainly determined by their chemical composition. The electrocatalytic properties of a composite PbO2-TiO2 anode vs the oxygen evolution reaction (OER) and the electrochemical degradation of methyl tert-butyl ether (MTBE) were investigated. Композиційні матеріали на основі PbO2, що мають в своєму складі TiO2 або ZrO2, були одержані з суспензійних електролітів з часточками дисперсної фази TiO2 чи ZrO2. Концентрація сторонніх оксидів в композиті залежить від складу електроліту та умов осадження. В процесі залучення часточок дисперсної фази до композиту кристали плюмбум(IV) оксиду зменшуються до субмікроних та нано-розмірів. Фізико-хімічні властивості та електрокаталітична активність композиційних матеріалів у більшості випадків обумовлюється їх хімічним складом. Досліджено електрокатілітичні властивості композиційних анодів PbO2-TiO2 в реакціях виділення кисню та електрохімічного руйнування метил трет-бутилового етеру (МТБЕ).