Role of the structure and composition of macromolecule chain in chemical plasticization of polymers

Abstract

The correlation between the parameters of chemically plasticized polar polymers (glass transition temperature, solubility parameter, cohesive energy, polarizability, modulus of elasticity in shear) with polarity and van der Waals volume of macromolecule link was investigated. It was shown that the chemical plasticization of PVAc and PVME by the alkylated polar groups replacement in weakly polar methyl group is not associated with the parameters of isolated macromolecule and is mainly determined by the intermolecular interaction. The chemical plasticization for the polyacid and polybase occurs via alkylation carboxyl and hydroxyl groups accordingly. The methyl ether of poly(acrylic acid) chemical plasticization is observed at increase of an alkyl radical size. Встановлена кореляція між характеристиками пластифікованих полярних аморфних полімерів (температурою склування, параметром розчинності, енергією когезії, поляризуємістю, модулем пружності при зсуві) з полярністю та Ван-дер-Ваальсовим об’ємом ланки макромолекули. Показано, що хімічна пластифікація полівінілацетету та полівінілметилового естеру заміною алкільованих полярних груп на слабо полярну метильну не пов’язана з параметрами ізольованої макромолекули, а визначається головним чином міжмолекулярною взаємодією. Для полікислоти та поліоснови хімічна пластифікація відбувається через алкілування відповідно карбоксильних та гідроксильних груп. Хімічна пластифікація метилового естеру поліакрилової кислоти спостерігається при збільшенні розміру алкільного радикалу.